Colloidal graphite

Type: S TF
Property: excellent high lubrication property,high conductivity,high absorption and high catalysis,and high plasticity.
Use: used as high temperature resistance lubricant base material,powder metallurgy carbon film resistance material,electrical contact alloy,and precious metal alloy material and more.

Technical index of Colloidal graphite :

*********************************************************

Conductive graphite

Special processing, the conductive graphite has the features of electrical conductivity, plasticity. Acid and alkali resistance, and stable chemical property against organic solvent corrosion. Currently, the product is widely used in manufacture of energy storage, Lithium ion, Nickel-metal hydride, Ni-Cd and alkaline zinc manganese batteries, as well as electronic components.

 Main Technical index :

Brand No.	Fixed carbon (%)	Ash (%)	Size (μm)	Moisture (%)
KS-75	≥99.98	≯0.02	75	≯0.1
KS-44	≥99.98	≯0.02	44	≯0.1
KS-15	≥99.98	≯0.02	15	≯0.1
KS-6	≥99.98	≯0.02	6	≯0.1

***********************************************************

Spherical graphite

Type: THD-12-40
Property: strong chemical stability, high charging/discharging capacity, long circle life, and eco-friendliness.
Use: mainly used in lithium ion secondary battery.

Main Technical index :

Item	Tap Density (g/cm3)	Specific Surface Area (m2/g)	Particle size (d50) (μm)	Carbon content (%)	Moisture (%)	Charging Capacity (mAh/g)	Coulomb Efficiency (%)	Cycle Index
Index	0.92-1.0	4-6.5	12-40	99.9-99.99	<0.1	>360	>90	≥800

*************************************************************

batter graphite coating

Type: DAG-1
Property: possesses good film forming and adhesiveness property,good electricity conductivity,firm coating,fast drying,and the coating after being dried can endure the erosion of 40% potassium hydroxide for long time.

Technical index of High energy batter graphite coating :

Propery	Technical index of	Main Use
Total solid(%≥)	38	It is mainly applied to inner wall of high energy alkali zinc and manganese battery,and forms an erosion resistance conductive film.It is a main raw  material in this type of battery.
Content graphite(%≥)	32
Volume Resistivity(Ω.cm≤)	1.9
Graphite particle less than 5μm(%≥)	90

**********************************************************************

Forging graphite lubricant

Type: MD-2、MD-2A、MD-7、MD-8、MD-12、MD-15.
Property: good lubrication property,release property and high temperature adhesiveness.It can improve the life length of mould and the quality of forged piece,and it does not pollute the environment and is easy to be used.

Main specification, physical and chemical indexs of Forging graphite lubricant :

Types	Property and index			Application example
	Total solid (%)≮	Content graphite (%)≮	Sedimentation degree after diluted 20 times for 3 hours
MD-2	28	20	35	Die forging,roller forging,gear rough and finish forging
MD-3	30	25	Not dilution	Molten steel casting sliding slate lubrication
MD-4	35	25	Not dilution	Used in pure silicon smelt
MD-7	40	25	40	Extrude and process light alloy
MD-8	30	23	35	Heavy presser die forging
MD-10	35	26	Not dilution	Warhead and cartridge case hot extrusion processing
MD-15	30	23	35	Hammer forging

The forging graphite lubricant manufactured by Tianhe is black color,and it is an ideal high temperature release mould lubricant for the heating of nonferrous metal,and widely used in forging and metal pressing and processing industry

**

Wire-drawing graphite lubricant

Type: thick wire,intermediate wire,fine wire and super fine wire
Specification: TS-O S-O S-1B S-1
Property: possesses good high temperature lubrication property,and protect mould to reduce abrasion.It is also of excellent high temperature application property,and does not flake off and burn in 600-1200℃,protect wire from oxidation.It is easy to store and does not erode.

Technical index of wire-drawing graphite lubricant of Wire-drawing graphite lubricant :

Propery	Technical index of				Main Use
	TS-O	S-O	S-1B	S-1
Content graphite(%≥)	14.5	17.5	19.5	21.5	It is an indispensable high temperature lubricant for metal such as tungsten, molybdenum, rhenium and thorium, and can also be used in coating agent in metal and glass casting or contact or resistance materials in electronic industry.
Solid Content(%≥)	17.0	20.0	24.5	24.0
Ash content in Solid Content(%≤)	1.0	2.0	2.0	2.0
Sedimenttation degree after 8 hours(%≤)	2.5	7.5	-	-
Sedimenttation degree after 3 hours(%≤)	-	-	7.5	7.5
Adhesiveness	Good	Good	Good	Good

*********

earthyl graphite

Amorphous graphite, also called aphanitic graphite, is provided by this company.

Carbon content: 80%-99.9%
Size: 200μm-0.5μm

***************************************

Special graphite powder for powder metallurgy

Type: -399 –399.9 TF
Property: oxidation resistance and self-lubrication function under the high temperature condition,can also increase the strength(hardness)of original piece.
Use: mainly used in powder metallurgy industry

Technical index of Special graphite powder for powder metallurgy:

Brand No.	Fixed Carbon≥(%)	Volatile constituent≤(%)	Moisture≤(%)	Particle Size
-399	99	1	0.3	90
-399.9	99.9		0.2	90
TF-1	99	1	0.3	6μm 70
TF-2	99	1	0.3	10μm 70

**********************************************************

Special graphite powder for carbon brush

Type: T295 T298 T299 T395 T398 T399
Property: good lubrication function property,low trace element,abrasion resistance and less electrical spark.
Use: used for all types of carbon brushe

Technical index of Special graphite powder for carbon brush :

Brand No.	Fixed Carbon≥(%)	Volatile constituent≤(%)	Moisture≤(%)	Particle Size
T295	95	1.2	0.3	200μm
T298	98	1	0.3	200μm
T299	99	1	0.3	200μm
T395	95	1.2	0.3	325μm
T398	98	1	0.3	325μm
T399	99	1	0.3	325μm